Authors: Vadivambal, R., V. Chelladurai, F. Jian and D.S. Jayas.
Identifier: C15224
Download file: https://library.csbe-scgab.ca/docs/journal/57/C15224.pdf
Published in: CBE Journal » CBE Journal Volume 57 (2015)
Temperature and humidity sensor-cables used in grain bins are currently made of steel or synthetic materials. The potential use of natural fibres as cables was tested. The natural fibres selected for this study were hemp and sisal. The tensile strength and extension of hemp and sisal ropes with diameters of 6, 8, or 10 mm were measured at various temperatures ranging from -40°C to +60°C. The hemp ropes had significantly higher tensile strength than the sisal ropes for all three tested diameters. The tensile strength of the fibres examined was not significantly affected by freezing temperatures but was significantly lowered at 60°C, and did not increase linearly with increase in diameter.
Les câbles des capteurs de température et d’humidité utilisés dans les silos à grains sont couramment faits d’acier ou de matériaux synthétiques. Le potentiel de deux fibres naturelles, le chanvre et le sisal, pour remplacer ces câbles a été évalué dans le cadre de cette étude. La résistance en traction et l’étirement de cordes de chanvre et de sisal d’un diamètre de 6, 8 ou 10 mm ont été mesurés à différentes températures variant de -40°C à +60°C. Pour les trois diamètres testés, les cordes de chanvre avaient une résistance en traction significativement plus élevée que celles de sisal. La résistance en traction des fibres étudiées n’était pas significativement modifiée à des températures sous le point de congélation. Toutefois, elle était significativement diminuée à 60°C et n’augmentait pas linéairement avec l’augmentation du diamètre.
chanvre, sisal, résistance en traction, câble, corde naturelle.